Dear Dr. Jorgen, I worked out the equations and have something interesting. In an FEA analysis with temperature changing with time - at each time-s...

14 years ago
Reply

Ok, I will probably use the time shift integral. But just to make sure, if I use the scaled time (or shifted time) in the evolution integral - then t...

14 years ago
Reply

Thanks for the reply. Would it be wrong to simply calculate the relaxation time at different temperature by the TRS model tau(T) = tau(Tref)A(T) and ...

14 years ago
Topic
Replies: 8
Views: 990
Reply

Jorgen, thanks for the reply. As I said I am new to experiments. I have some very conceptual issues regarding performing the test. - Is it ok to app...

14 years ago
Topic
Replies: 2
Views: 449
Topic
Replies: 1
Views: 401
Reply

Thanks for the reply Jorgen. For the third approach, is it sufficient to perform a uniaxial compression test with about 1% strain? And then simply ca...

15 years ago
Reply

Thanks for the reply Dr. Jorgen. 1) I have developed a fitting procedure for the cylindrical compression test (uniaxial compression, about 1% elongat...

15 years ago
Reply

Frank, I took a look at your thesis. I think your analysis was tailored using a constant strain rate or increasing strain. I have always been unde...

15 years ago
Reply

Dear Frank, Thanks for your reply. I have read the papers by Jain et. al but it somehow seemed different than what I am trying to do. I will go t...

15 years ago
Reply

Dr Jorgen, I am studying glass. To be precise, its an N-BK7 glass by Edmunds. The transition temperature can be between 450-550C. I am interested in...

15 years ago