bw_composite
@bw_composite
Estimable Member
Joined: Aug 29, 2007
Last seen: Oct 1, 2019
Topics: 38 / Replies: 86
Reply

Hi Jorgen, just to wrap this one up (an alternative solution was found), I wanted to answer your query about incompressibility. The base element mat...

15 years ago
Reply

Jorgen, thanks for your reply. I have done some trials tuning the time steps, with little luck. Regretfully I am not wawre of options to improve th...

15 years ago
Reply

Hi Jorgen, thanks for the reply. the tbdata command in question determines: first value: how much, in percentage, is lost (shear modulus wise) in ...

15 years ago
Reply

Hi, I do not have references to any academic work, but thought it would not harm if a method we have sometimes used is presented.This might or not b...

15 years ago
Reply

Hi there, the choice of the elemnt to plot on is something which depends on the aim of your work. From what you say it looks like you are interested...

15 years ago
Reply

Rm447, thanks for your clarification, I wrongly assumed the surface was geometrically defined (actually my advice refreed to the trivial case of a pl...

15 years ago
Reply

Hi there, I will step in on this one hoping I can help a bit. From your plot I would say strains will not be uniform, which might happen in an engin...

15 years ago
Reply

Mccasillo, I found your post timely as I am learning how to model viscolelasticity in ANSYS. I do not quite understand one of the ways ANSYS uses in...

15 years ago
Reply

Hi All, I am not sure I have understood the query, but I will give my best shot. If what is needed are the numeric results for stresses / displaceme...

16 years ago
Reply

Jorgen, many thanks for this clarification Muzialis

16 years ago
Reply

Jorgen, your last comment about crazy stresses sounds very interesting but regretfully I do not think I understand it at all. Would you mind extendi...

16 years ago
Reply

Jorgen, thanks for your reply. I do not regretfully have nay experience in user defined materials. Might be a good occasion to start thinking about ...

16 years ago
Reply

Jorgen, thanks for your reply. My question was badly posed indeed, certainly there is not a best test. I am just trying to understand which one rep...

16 years ago
Reply

Jorgen, thanks for your reply. My question was badly posed indeed, certainly there is not a best test. I am just trying to understand which one rep...

16 years ago
Reply

Jorgen, many thanks for your reply. Just to close this thread, what would then the most rigorous way of determining the shear modulus relaxation be?...

16 years ago