Hi there, I think the source you attached is plainly badly written. They clearly state Table 2 should contain the fitted values for the cases plotte...

5 years ago
Topic
Replies: 2
Views: 505
Reply

Dear Martin, in reference to your points: 1. any deformation on elastic materials can be decomposed in volumetric (volume changing) and distorsional ...

9 years ago
Reply

Hi there, I would like to throw my thoughts in. Your problem is quite complex. When compressed above a certain threshold, rubber in compression can p...

9 years ago
Reply

Dear Tarup, in reference to your first point about linear viscoelasticity, there are very easy ways to check if linear viscoelasticity can be applied...

9 years ago
Topic
9 years ago
Replies: 3
Views: 653
Topic
9 years ago
Replies: 1
Views: 556
Reply

Hello David, I do hope I am not being rude or generally inappropriate, may I suggest a very useful reference, Viscoelastic solids by Prof. R. Lakes....

9 years ago
Topic
9 years ago
Replies: 2
Views: 482
Reply

Mr. Inventor, I am really unsure that would work. The equation you point at is not objective, i.e. frame independent. One could look at a state of sh...

11 years ago
Reply

Mr. Inventor, that is an interesting paper, but how do you put it at use? The deformation measure they introduced is local!

11 years ago
Reply

I see your problem now, one I am quite familiar with! Back to your problem, I am not so sure I understand your plan. If you compare principal stretch...